PVC waterproof membranes
with fiber (PVC-L )
Products Description
The PVC waterproofing rolls formulas are based upon polyvinyl chloride resin with other assistants added to provide flexibility and stability such as anti-oxidant,absorbent of ultraviolet light, plasticizer and plastic filling ag PVC waterproofing membrane is a highly-engineered,new-type membrane manufactured using polyvinyl chloride as main materials and added other chemicals such as anti-oxidant,anti-UV materials to make it flexible,stable and UV-resistant.
Product Features
1. Excellent weathering characteristics,
2.High tensile strength and long-term flexibility.
3. Excellent resistance to harsh chemicals and industrial pollutants.
4.Heat or solvent-welding effectively provides seamless roof coverings
5.Can be choice for various methods of attachment and any shape of roof
Products Specification
Name
|
Thickness(mm)
|
Width(m)
|
Length(m)
|
PVC-L
|
1.2-2.0
|
2
|
20
|
Technical Parameters GB12952-2010
No.
|
Test Item
|
Indicators
|
H
|
L
|
P
|
G
|
GL
|
1
|
The thickness of resin layer above the reinforcement fabric mm≥
|
—
|
0.40
|
2
|
Stretching Performance
|
Maximum Tension N/cm ≥
|
—
|
120
|
250
|
|
120
|
Tension Strength Mpa≥
|
10
|
—
|
—
|
10
|
—
|
Max. Tension Elongation %≥
|
—
|
—
|
15
|
—
|
—
|
Breaking Elongation%≥
|
200
|
150
|
—
|
200
|
100
|
3
|
Heating Treatment Size Change Rate%≤
|
2.0
|
1.0
|
0.5
|
0.1
|
0.1
|
4
|
Low-temperature Bending
|
-25â
-25â No Craze
|
5
|
Water Impermeability
|
Water Impermeability
|
6
|
Impact Resistance
|
Water Impermeability
|
7
|
Anti-static Load a
|
—
|
—
|
Water Impermeability
|
8
|
Seam Peel Strength N/mm ≥
|
4.0 or Membrane Breaking
|
3.0
|
9
|
Right-angle Tear Strength N/mm ≥
|
50
|
—
|
—
|
50
|
—
|
10
|
Trapezoid Tear Strength N≥
|
|
150
|
250
|
|
220
|
11
|
water absorptionï¼70â168hï¼ï¼
|
After Soaking ≤
|
4.0
|
After Airing≥
|
-0.40
|
12
|
Heat agingï¼80âï¼
|
Time
|
672h
|
Appearance
|
No blisters, cracks, delamination, bonding and holes
|
Tensile Strength ï¼max. tensileï¼Retention%≥
|
85
|
Elongation Retention %≥
|
80
|
Cold Bending
|
No Craze
|
13
|
Chemical Resistance
|
Appearance
|
No blisters, cracks, delamination, bonding and holes
|
Tensile Strength ï¼max. tensileï¼Retention %≥
|
85
|
Elongation Retention %≥
|
80
|
Cold Bending
|
No Craze
|
14
|
Artificial climate accelerating ageing c
|
Time
|
1500hb
|
Appearance
|
No blisters, cracks, delamination, bonding and holes
|
Tensile Strength ï¼max. tensileï¼Retention %≥
|
85
|
Elongation Retention ﹪≥
|
80
|
Cold Bending
|
No Craze
|
a Anti-static loading is only applied to the roofing membrane.
bThe artificial climate accelerated time is 2500 hours for single roofing membrane.
c Artificial climate accelerating ageing test is only apply to exposure membrane.
|
Application Range
PVC membranes form an effective barrier to liquid water or water vapor in the roof construction for industrial and civil engineering, underground engineering such as subway & tunnel, water conservancy such as water pools & ditch, shelter, grain depot, land filling, dyke, sewage treatment and basement.